1. Products Description
Micro grain raw material
Grain size: 0.4-0.6μm
Co 10%, 12%
TRS >3600 N/mm2
Hardness HRA 91.8-92.5
Work piece HRC45-50 HRC55-60 HRC65 HRC68
Helix angle 30°-45 °
Diameter of cutting edge 0.2-0.9 mm; 1-20 mm
Diameter of rods 4-20 mm
Length 50-100 mm
Cutting Form Flat, Square, Ball nose, Corner Radius, Taper Flute, etc
Flutes No. 1-7
HRC45 | HRC55 | HRC60 | HRC65 |
Grain Size:0.6um Co:10 % Flexural strength:3350N/mm2 |
Grain Size:0.6um Co:10 % Flexural strength:4000N/mm2 |
Grain Size:0.5um Co:12 % Flexural strength:4300N/mm2 |
Grain Size:0.4um Co:12.5 % Flexural strength:4300N/mm2 |
2. Application
Used for cutting Carbon steel, Tool steel, Mould steel, Stainless steel, Titanium alloy, Copper, Cast Iron and Aluminium, etc.
Grinding equipment: WALTER, ANCA, ROLLOMATIC
Testing equipment: ZOLLER
3. Coating
4. Packing
Brand Laser printed on cutter shank, 1 pcs in a plastic tube, 10 pcs a group
5. Delivery time
Keep stock for regular types
Samples: 3 - 5 days
Regular orders: 7 - 10 days
Coating |
Color |
Coating Temperature |
Thickness (um) |
HV |
Application Temperature |
Friction coefficient |
TiAlN |
Purple-Gray | <600°C | 3-5 | 3300 | 800 °C | 0.3 |
AlTiN | Black | <600 °C | 3-5 | 3500 | 900 °C | 0.3 |
TiSiN | Copper | <600 °C | 3-5 | 3500 | 1500 °C | 0.4 |
NaNo | Blue | <600 °C | 3-5 | 3800 | 1200 °C | 0.4 |
CrN | Silver Gray | <480 °C | 2-2.5 | 2500 | 700 °C | 0.3 |